Introduction:
STELLITE 6 is the most widely used of the wear resistant cobalt-based alloys and exhibits good all-round performance. It is regarded as the industry standard for general-purpose wear resistance applications.
C | Cr | Si | W | Fe | Mo | Ni | Mn | B | Co |
1.2 | 28 | 1.1 | 4.5 | 3 | 3 | 1 | bal | ||
*The chemical composition shown above is an outline only,and should not be taken as a full specification. *Note that cored wire may have higher Fe contents than other product forms. |
Density (lb/in³) |
Specific Gravity |
Solidus | Liquidus | Specific heat (J/kg·K) |
Magnetic Permeability |
Electrode Potential |
Electrical Conductivity |
Electrical Resistivity |
0.305 | 8.46 | 2340°F | 2540°F | 0.101°F Btu/lb- |
<1.2@200 Oersteds |
-0.25 Volts |
1.9%IACS (Int. Annealed Copper Std.) |
41.73 microhms-inch |
Thermal Expansion Coefficient | Thermal Conductivity by Temperature | ||||||
°F | Microinch/ inch-°F |
°C | Microns/ m-°C |
°F | Btu/ft2/in/ hr/°F |
°C | W/mk |
212 | 6.3 | 100 | 11.34 | 70 | 102.7 | 21.11 |
14.82 |
Contact Person: Miss. Bella Hu
Tel: 86--13897908592
Fax: 86-24-22902706
Cobalt Chrome Alloy Sleeve Powder Metallurgy And Casting Process Manufacture
Precision Machining Cobalt Alloy 6 Seat Ring Upon Drawing 38 - 48 HRC Hardness
Steel Liquid Cobalt Alloy 6 Welding Rod Tube / Salt Bath Temperature Measurement
High precision Cobalt Base Alloy 6 , Cobalt Chrome Alloy Cylinder Bushing
Gas Equipment Parts Cobalt Chrome Alloy , Cobalt Chromium Molybdenum Alloy
Spare Parts Chrome Cobalt Alloy 38HRC - 55HRC Hardness
Cobalt Tungsten Chromium Alloy Plate / Bars , Surface Finish Cast Cobalt Alloys
Corrosion Resistance Cobalt Chrome Alloy Metal Bushing Powder Metallurgy Process
High Fusion Welding Resistance Tungsten Silver Alloy Powder Pressing Processing
Customized Silver Tungsten Alloy , Silver Tungsten Contacts / Electrodes
Bright Surface AgW Silver Tungsten Alloy Electrrode Contacts High Conductivity
High Durability Silver Tungsten Alloy Round Bar / Welding Rod High Temperature Resistance