Tungsten Copper Alloy?Tungsten-copper alloys (copper-tungsten alloys, CuW or WCu) are pseudo-alloys of copper and tungsten. Since copper and tungsten cannot dissolve each other, the material consists of different particles of a metal dispersed in a matrix of another metal. The alloy combines the properties of both metals to provide heat resistance, ablation resistance, high thermal conductivity and electrical conductivity, and ease of processing. The member is made of a WCu alloy by pressing the tungsten particles into a desired shape, sintering the compacted portion, and then infiltrating with molten copper. Alloy sheets, rods and bars are also available.
| Type | Density (g/cm3) | Conductivity | HB (MPa) | Size (mm) |
| WCu50 | 11.9~12.3 | ≥55 %IACS | 1130~1180 | Rod: Ø1~50 Length<300 Sheet: Width<190 Length<300 Special type: Width<190 Length<300 |
| WCu40 | 12.8~13.0 | ≥47 %IACS | ≥1375 | |
| WCu30 | 13.8~14.4 | ≥42 %IACS | ≥1720 | |
| WCu20 | 15.2~15.6 | ≥34 %IACS | ≥2160 | |
| WCu10 | 16.8~17.2 | ≥27 %IACS | ≥2550 | |
| WCu7 | 17.3~17.8 | ≥26 %IACS | ≥2900 |
The tungsten and copper parts we offer have these characteristics. The electrical and thermal properties of the alloy vary with different ratios. Copper increases thermal conductivity, which plays a large role in circuit breakers. The resistivity increases as the tungsten content of the alloy increases. When the alloy contains 90% tungsten, the tungsten content is 3.16% and the tungsten content is 6.1%. The increase in tungsten leads to an increase in ultimate tensile strength until the alloy reaches 80% tungsten and 20% copper with an ultimate tensile strength of 663 MPa. After this mixture of copper and tungsten, the ultimate tensile strength then begins to decrease quite rapidly.
Shenyang Top New Material Co Ltd
Add：NO.35, xingnong Road,Shenbei Dist ,Shenyang ,China
Tel:+86-18002461961 Fax:+86-24-22902706
Skype: ieleanor2012
Web: www.cobaltalloy.com Email: elleworld@sytop.cn
Contact Person: Miss. Bella Hu
Tel: 86--13897908592
Fax: 86-24-22902706
Cobalt Chrome Alloy Sleeve Powder Metallurgy And Casting Process Manufacture
Precision Machining Cobalt Alloy 6 Seat Ring Upon Drawing 38 - 48 HRC Hardness
Steel Liquid Cobalt Alloy 6 Welding Rod Tube / Salt Bath Temperature Measurement
High precision Cobalt Base Alloy 6 , Cobalt Chrome Alloy Cylinder Bushing
Gas Equipment Parts Cobalt Chrome Alloy , Cobalt Chromium Molybdenum Alloy
Spare Parts Chrome Cobalt Alloy 38HRC - 55HRC Hardness
Cobalt Tungsten Chromium Alloy Plate / Bars , Surface Finish Cast Cobalt Alloys
Corrosion Resistance Cobalt Chrome Alloy Metal Bushing Powder Metallurgy Process
High Fusion Welding Resistance Tungsten Silver Alloy Powder Pressing Processing
Customized Silver Tungsten Alloy , Silver Tungsten Contacts / Electrodes
Bright Surface AgW Silver Tungsten Alloy Electrrode Contacts High Conductivity
High Durability Silver Tungsten Alloy Round Bar / Welding Rod High Temperature Resistance